Resonance Properties of the Y0:5Sr0:5Cr0:5Mn0:5O3 Polycrystal
Автор:
Mataev, Mukhametkali M.
Patrin, Gennadiy S.
Seitbekova, Karima Zh.
Shiyan, Yaroslav G.
Churkin, Viktor R.
Матаев, Мухаметкали М.
Патрин, Геннадий С.
Сейтбекова, Карима Ж.
Шиян, Ярослав Г.
Чуркин, Виктор Р.
Дата:
2024-12Журнал:
Журнал Сибирского федерального университета. Математика и физика 2024 17(6). Journal of Siberian Federal University. Mathematics & Physics 2024 17(6)Аннотация:
This work presents the results of the experimental studies of the magnetic resonance prop-
erties of the Y0:5Sr0:5Cr0:5Mn0:5O3 polycrystalline system. We found that two absorption lines are
observed in the magnetic ordering region at T < 80 K in the spectrum. When changing to the paramag-
netic region, one of the lines disappears, but a set of weak lines appears, which are identified as belonging
to the Mn2+ impurity ions. The temperature behavior of the main peak line width is analyzed within
the framework of the single-ion relaxation theory. Mn3+ ions were found to be responsible for the low-
temperature peak, and Cr4+ ions are responsible for the high-temperature peak. The constants of the
molecular fields acting on the Mn3+ and Cr4+ subsystems have been determined В работе представлены результаты экспериментальных исследований магниторезонансных свойств поликристаллической системы Y0:5Sr0:5Cr0:5Mn0:5O3. Получено, что области магнитного упорядочения при T < 80 K в спектре наблюдается две линии поглощения. При переходе
в парамагнитную область одна из линий исчезает, но появляются набор слабых линий, идентифицируемых как принадлежащие примесным ионам Mn2+. В рамках теории одноионной релаксации
проведен анализ температурного поведения ширины линии основного пика. Установлено, что за
низко температурный пик ответственны ионы Mn3+, а за высокотемпературный –– ионы Cr4+.
Определены константы молекулярных полей, действующих на подсистемы ионов Mn3+ и Cr4+