Resonance Properties of the Y0:5Sr0:5Cr0:5Mn0:5O3 Polycrystal

Abstract

This work presents the results of the experimental studies of the magnetic resonance prop- erties of the Y0:5Sr0:5Cr0:5Mn0:5O3 polycrystalline system. We found that two absorption lines are observed in the magnetic ordering region at T < 80 K in the spectrum. When changing to the paramag- netic region, one of the lines disappears, but a set of weak lines appears, which are identified as belonging to the Mn2+ impurity ions. The temperature behavior of the main peak line width is analyzed within the framework of the single-ion relaxation theory. Mn3+ ions were found to be responsible for the low- temperature peak, and Cr4+ ions are responsible for the high-temperature peak. The constants of the molecular fields acting on the Mn3+ and Cr4+ subsystems have been determined

В работе представлены результаты экспериментальных исследований магниторезонансных свойств поликристаллической системы Y0:5Sr0:5Cr0:5Mn0:5O3. Получено, что области магнитного упорядочения при T < 80 K в спектре наблюдается две линии поглощения. При переходе в парамагнитную область одна из линий исчезает, но появляются набор слабых линий, идентифицируемых как принадлежащие примесным ионам Mn2+. В рамках теории одноионной релаксации проведен анализ температурного поведения ширины линии основного пика. Установлено, что за низко температурный пик ответственны ионы Mn3+, а за высокотемпературный –– ионы Cr4+. Определены константы молекулярных полей, действующих на подсистемы ионов Mn3+ и Cr4+