Synthesis and Magnetic Properties of Crystals Bi₂BaFe₄O₁ ₀
View/ Open:
URI (for links/citations):
https://elib.sfu-kras.ru/handle/2311/71752Author:
Mataev, Mukhametkali M.
Patrin, Gennady S.
Abdraymova, Moldir R.
Tursinova, Zhanar I.
Yurkin, Gleb Yu.
Матаев, Мухаметкали М.
Патрин, Геннадий С.
Абдраймова, Молдир Р.
Турсинова, Жанар И.
Юркин, Глеб Ю.
Date:
2018-08Journal Name:
Журнал Сибирского федерального университета. Математика и физика. Journal of Siberian Federal University. Mathematics & Physics;2018 11 (4)Abstract:
The paper presents the results of an experimental study of the first synthesized compound in the system
Bi2O3-BaO-Fe2O3. It was found that the compound has cubic symmetry, the lattice parameters was
determined. Electron microscopy measurements reveal that, in general, elemental composition of different
parts of the samples corresponds to Bi2BaFe4O10 formula. According to magnetic measurements, the
compound has a magnetic order with the magnetic ordering temperature TC = 700 K В работе представлены результаты экспериментального исследования впервые синтезированного соединения в системе Bi2O3-BaO-Fe2O3. Установлено, что полученное соединение имеет кубическую симметрию, определены параметры решетки. Методом электронно-микроскопических
измерений получено, что в целом элементный состав, измеренный в разных частях образцов, соответствует формуле Bi2BaFe4O10. Из магнитных измерений следует, что соединение имеет
магнитный порядок с температурой магнитного упорядочения TC = 700 K