Crystallization Kinetics and Magnetic Properties of Fe₈₀₋ₓCoₓP₁₄B₆ Metallic Glasses
View/ Open:
URI (for links/citations):
https://elib.sfu-kras.ru/handle/2311/68977Author:
Prahova, Darja A.
Grishin, Alexander M.
Ignahin, Vladimir S.
Lugovskaya, Lyubov A.
Osaulenko, Roman N.
Прахова, Дарья А.
Гришин, Александр М.
Игнахин, Владимир С.
Луговская, Любовь А.
Осауленко, Роман Н.
Date:
2018-03Journal Name:
Журнал Сибирского федерального университета. Математика и физика. Journal of Siberian Federal University. Mathematics & Physics;2018 11 (1)Abstract:
We report about formation mechanism, crystallization kinetics and magnetic properties observed in the
series of rapidly solidified Fe₈₀₋ₓCoₓP₁₄B₆ metallic glasses with x = 25, 32, 35 and 40 at.%. Magnetic
soft Fe₈₀₋ₓCoₓP₁₄B₆ metallic glasses have 15–25 m thick and 2–8 mm wide. The ribbon samples were
created to meltspun onto the massive copper wheel from the RF-melted superheated master ingots В настоящей работе показаны основы механизма кинетики кристаллизации быстрозакаленных металлических стекол на основе Fe₈₀₋ₓCoₓP₁₄B₆ при x = 25, 32, 35 и 40 at.%. В ходе работы была получены магнитомягкие металлические стекла медотом быстрой закалки на диске из жидкого
состояния. Полученные ленты обладают толщиной порядка 15–25 m и шириной около 2–8 mm