Properties and Biocompatibility of Poly-3-Hydroxybutyrate-co-3-Hydroxyvalerate/ Poly-ε-Caprolactone Blends
Скачать файл:
URI (для ссылок/цитирований):
https://elib.sfu-kras.ru/handle/2311/20182Автор:
Boyandin, Anatoly N.
Nikolaeva, Elena D.
Sukovatiy, Aleksey G.
Бояндин, А.Н.
Николаева, Е.Д.
Суковатый, А.Г.
Дата:
2016-03Аннотация:
Blends consisting of the poly-3-hydroxybutyrate-co-3-hydroxyvalerate (PHBV) copolymer and poly-
ε-caprolactone (PCL) were used to prepare polymer films by casting solution technique. The structure
and physical-mechanical, and biological properties of the films were examined as influenced by the
ratios of the blend components. The microstructure of the films was determined by the dominant
component: the films had porous surface if the percentage of PHBV was higher than that of PCL
and were relatively smooth if the dominant component was PCL. The highest elongation at break
(190-368 %) was exhibited by the films prepared from the blends containing 5-25 % PHBV; at 25 %
PHBV, local maxima of tensile strength (16 MPa) and Young’s modulus (529 MPa) were observed.
Biocompatibility of the films prepared from the blends was studied in the culture of NIH 3T3 mouse
fibroblast cells. Results of SEM and DAPI staining, determination of the number of attached cells, and
MTT assay showed the absence of cytotoxic effects and high cell adhesion and proliferation, which in
some cases were higher than on films prepared from pure PHBV and PCL. Thus, PHBV/PCL blends
are suitable materials for constructing cell scaffolds for tissue engineering and other reconstructive
technologies Смеси, состоящие из сополимера поли-3-гидроксибутирата-3-гидроксивалерата (ПГБВ) и
поли-ε-капролактона (ПКЛ), были использованы для получения полимерных пленок методом
испарения из раствора. Исследованы структура, физико-механические и биологические
свойства пленок в зависимости от соотношения компонентов смеси. Микроструктура
пленок определялась преобладающим компонентом: пленки имели пористую поверхность, если
содержание ПГБВ было выше, чем ПКЛ, и относительно гладкими при преобладании ПКЛ.
Наибольшее значение удлинения на разрыв (190-368 %) отмечалось для пленок, полученных
из смесей с содержанием 5-25 % ПГБВ; при 25 % ПГБВ наблюдались локальные максимумы
предела прочности на разрыв (16 МПа) и модуля Юнга (529 МПа). Биосовместимость
полученных из смесей пленок была изучена в культуре фибробластов мыши линии NIH
3T3. Результаты растровой электронной микроскопии, окрашивания DAPI, определения
численности прикрепленных клеток и MTT-тест показали отсутствие цитотоксических
эффектов и высокий уровень адгезии и пролиферации клеток, в ряде случаев превосходившие
соответствующие значения для пленок, приготовленных из чистых ПГБВ и ПКЛ. Таким
образом, смеси ПГБВ/ПКЛ являются материалами, подходящими для конструирования
клеточных матриксов для тканевой инженерии и других реконструктивных технологий
Коллекции:
Метаданные:
Показать полную информациюСвязанные материалы
Показаны похожие ресурсы по названию, автору или тематике.
-
Synthesis and Properties of Polymers Based on Styrene and α-angelicalactone
Kaigorodov, Konstantin L.; Tarabanko, Valery E.; Loskutov, Sergei R.; Mazurova, Elena V.; Kondrasenko, Alexander A.; Voronchikhin, Vasiliy D.; Smirnova, Marina A.; Malyar, Yuri N.; Vigul, Dmitry O.; Кайгородов, К. Л.; Тарабанько, В. Е.; Лоскутов, С. Р.; Мазурова, Е. В.; Кондрасенко, А. А.; Ворончихин, В. Д.; Смирнова, М. А.; Маляр, Ю. Н.; Вигуль, Д. О. (Сибирский федеральный университет. Siberian Federal University, 2022-03)Polyangelicalactone-graft-polystyrene copolymers were obtained through cationic polymerization. Increasing the portion of styrene units in the copolymers improves the strength properties and increases fragility. Increasing ... -
Biodegradation of Polymers Based on Styrene and Polyangelicalactone
Kaigorodov, Konstantin L.; Tarabanko, Valery E.; Pashenova, Nataliya V.; Loskutov, Sergei R.; Mazurova, Elena V.; Voronchikhin, Vasiliy D.; Smirnova, Marina A.; Кайгородов, К. Л.; Тарабанько, В. Е.; Пашенова, Н. В.; Лоскутов, С. Р.; Мазурова, Е. В.; Ворончихин, В. Д.; Смирнова, М. А. (Сибирский федеральный университет. Siberian Federal University, 2022-06)Polyangelicalactone-graft- polystyrene copolymers (PAL‑graft-PS) were obtained through cationic polymerization. The resulting copolymers were completely destroyed when incubated in gray forest soil over 28 weeks. ... -
Микробиологическая деградация поли-3-гидроксибутирата в образцах агрогеннопреобразованных почв
Виноградова, О.Н.; Прудникова, С.В.; Зобова, Н.В.; Колесникова, В.Л.; Vinogradova, Olga N.; Prudnikova, Svetlana V.; Zobova, Natalya V.; Kolesnikova, Valentina L. (Сибирский федеральный университет. Siberian Federal University., 2015-06)Исследована деградация поли-3-гидроксибутирата (П3ГБ) в лабораторных условиях в полевой и огородной почвах с различной структурой микробиоценозов. В огородной почве с высоким содержанием элементов питания общая численность ... -
Реконструкция модельных дефектов нижней стенки глазной орбиты лабораторных животных с применением резорбируемых 3d-пластин
Лазаренко, В.И.; Шумилова, А.А.; Проскурин, Е.В.; Волков, В.А.; Кириченко, А.К.; Шишацкая, Е.И.; Lazarenko, Viktor I.; Shumilova, Anna A.; Proskurin, Yegor V.; Volkov, Vladimir A.; Kirichenko, Andrei K.; Shishatskaya, Ekaterina I. (Сибирский федеральный университет. Siberian Federal University., 2016-03)В работе исследованы резорбируемые полимерные 3D-пластины на основе полиэфира гидроксимасляной кислоты – поли-3-гидроксибутирата (П(3ГБ)) в сравнении с коммерческим препаратом ООО “Пластика” (аллохрящ) для реконструкции ... -
Дифференцировка ммск в остеобласты на пористых 3D-носителях из поли-3-гидроксибутирата
Шумилова, А.А.; Николаева, Е.Д.; Shumilova, Anna A.; Nikolaeva, Elena D. (Сибирский федеральный университет. Siberian Federal University., 2016-03)В настоящей статье разработаны и исследованы экспериментальные пористые 3D-носители из разрушаемого природного полимера 3-гидроксимасляной кислоты [П(3ГБ)], предназначенные для восстановления дефектов костной ткани. ...