Biodegradation of Polymers Based on Styrene and Polyangelicalactone
Скачать файл:
URI (для ссылок/цитирований):
https://elib.sfu-kras.ru/handle/2311/145622Автор:
Kaigorodov, Konstantin L.
Tarabanko, Valery E.
Pashenova, Nataliya V.
Loskutov, Sergei R.
Mazurova, Elena V.
Voronchikhin, Vasiliy D.
Smirnova, Marina A.
Кайгородов, К. Л.
Тарабанько, В. Е.
Пашенова, Н. В.
Лоскутов, С. Р.
Мазурова, Е. В.
Ворончихин, В. Д.
Смирнова, М. А.
Дата:
2022-06Журнал:
Журнал Сибирского федерального университета. Химия. Journal of Siberian Federal University. Chemistry 2022 15 (2)Аннотация:
Polyangelicalactone-graft-
polystyrene
copolymers (PAL‑graft-PS)
were obtained through
cationic polymerization. The resulting copolymers were completely destroyed when incubated in gray
forest soil over 28 weeks. Individual strains of fungi destroyed the copolymer partially within 13 weeks;
the most active among the studied cultures was Leptographium sp. The biodegradation products of
copolymers do not statistically have a toxic effect. The obtained results show that the modification of
polystyrene (PS) with the impurities of polyangelicalactone (PAL) gives them biodegradation abilities
and does not worsen the properties of the copolymers Получены привитые сополимеры стирола с полиангеликалактоном (PAL‑graft-PS)
методом катионной полимеризации. Установлено, что сополимеры полностью разрушаются
при инкубации в серой лесной почве в течение 28 недель. Отдельные штаммы грибов
частично разрушали сополимер в течение 13 недель; среди изученных культур наиболее
активна Leptographium sp. Продукты биоразложения сополимеров и блок-сополимеров
статистически не обладают токсическим действием. Полученные результаты показывают, что
модификация полистирола (PS) примесями полиангеликалактона (PAL) придает им способность
к биоразложению, не ухудшая свойства
сополимеров
Коллекции:
Метаданные:
Показать полную информациюСвязанные материалы
Показаны похожие ресурсы по названию, автору или тематике.
-
Synthesis and Properties of Polymers Based on Styrene and α-angelicalactone
Kaigorodov, Konstantin L.; Tarabanko, Valery E.; Loskutov, Sergei R.; Mazurova, Elena V.; Kondrasenko, Alexander A.; Voronchikhin, Vasiliy D.; Smirnova, Marina A.; Malyar, Yuri N.; Vigul, Dmitry O.; Кайгородов, К. Л.; Тарабанько, В. Е.; Лоскутов, С. Р.; Мазурова, Е. В.; Кондрасенко, А. А.; Ворончихин, В. Д.; Смирнова, М. А.; Маляр, Ю. Н.; Вигуль, Д. О. (Сибирский федеральный университет. Siberian Federal University, 2022-03)Polyangelicalactone-graft-polystyrene copolymers were obtained through cationic polymerization. Increasing the portion of styrene units in the copolymers improves the strength properties and increases fragility. Increasing ... -
Properties and Biocompatibility of Poly-3-Hydroxybutyrate-co-3-Hydroxyvalerate/ Poly-ε-Caprolactone Blends
Boyandin, Anatoly N.; Nikolaeva, Elena D.; Sukovatiy, Aleksey G.; Бояндин, А.Н.; Николаева, Е.Д.; Суковатый, А.Г. (Сибирский федеральный университет. Siberian Federal University., 2016-03)Blends consisting of the poly-3-hydroxybutyrate-co-3-hydroxyvalerate (PHBV) copolymer and poly- ε-caprolactone (PCL) were used to prepare polymer films by casting solution technique. The structure and physical-mechanical, ... -
Микробиологическая деградация поли-3-гидроксибутирата в образцах агрогеннопреобразованных почв
Виноградова, О.Н.; Прудникова, С.В.; Зобова, Н.В.; Колесникова, В.Л.; Vinogradova, Olga N.; Prudnikova, Svetlana V.; Zobova, Natalya V.; Kolesnikova, Valentina L. (Сибирский федеральный университет. Siberian Federal University., 2015-06)Исследована деградация поли-3-гидроксибутирата (П3ГБ) в лабораторных условиях в полевой и огородной почвах с различной структурой микробиоценозов. В огородной почве с высоким содержанием элементов питания общая численность ... -
Реконструкция модельных дефектов нижней стенки глазной орбиты лабораторных животных с применением резорбируемых 3d-пластин
Лазаренко, В.И.; Шумилова, А.А.; Проскурин, Е.В.; Волков, В.А.; Кириченко, А.К.; Шишацкая, Е.И.; Lazarenko, Viktor I.; Shumilova, Anna A.; Proskurin, Yegor V.; Volkov, Vladimir A.; Kirichenko, Andrei K.; Shishatskaya, Ekaterina I. (Сибирский федеральный университет. Siberian Federal University., 2016-03)В работе исследованы резорбируемые полимерные 3D-пластины на основе полиэфира гидроксимасляной кислоты – поли-3-гидроксибутирата (П(3ГБ)) в сравнении с коммерческим препаратом ООО “Пластика” (аллохрящ) для реконструкции ... -
Дифференцировка ммск в остеобласты на пористых 3D-носителях из поли-3-гидроксибутирата
Шумилова, А.А.; Николаева, Е.Д.; Shumilova, Anna A.; Nikolaeva, Elena D. (Сибирский федеральный университет. Siberian Federal University., 2016-03)В настоящей статье разработаны и исследованы экспериментальные пористые 3D-носители из разрушаемого природного полимера 3-гидроксимасляной кислоты [П(3ГБ)], предназначенные для восстановления дефектов костной ткани. ...