Analysis of the Effect of pH on the Stability and Optical Spectra of Au Nanoparticles Linked by Conductive BPE Molecule

Abstract

The preparation of detergent-free gold NPs by the citrate method is shown. The procedure of functionalization of monomeric Au NPs with 1,2-bis(2-pyridyl)ethylene (termed BPE) molecule to obtain Au-BPE dimers is described. According to the results of TEM analysis, the shape of the obtained NPs is close to spherical with a diameter of 21.94 0.28 nm. In dimers, the distance between NPs is controlled by the linker and is 0.75 0.12 nm, which is in agreement with the dimensions of the BPE molecule. According to the results of Experimental absorption UV-Vis spectra, measured over time, in 0.15 M nitric acid solution, Au-BPE dimers are more stable than in an alkali solution of the same molarity. Long-term exposure leads to a decrease in the intensity of the LSP peak of the dimers

Показано получение золотых наночастиц (Au НЧ) цитратным методом. Описана процедура функционализации мономерных Au НЧ молекулой 1,2-бис(2-пиридил)этилена (называемой BPE) для получения димеров Au-BPE. По результатам анализа ПЭМ форма полученных НЧ близка к сферической с диаметром 21,94 0,28 нм. В Au-BPE димерах расстояние между частицами контролируется линкером и составляет 0,75 0,12 нм, что согласуется с размерами молекулы BPE. По результатам экспериментальных UV-Vis спектров поглощения, измеренных от времени, в 0,15 М растворе азотной кислоты Au-BPE димеры более стабильны, чем в щелочном растворе той же молярности. Длительное воздействие приводит к снижению интенсивности пика LSP димеров