2013-06Abstract:
Issues related to engineering and application of composites based on nanodiamonds and degradable
polyhydroxyalkanoates are discussed. The ability of composite engineering is demonstrated on the
3-polyhydroxybutyrate microspheres – modified detonation nanodiamonds composite fabricated
through the bimolecular nucleophilic addition (AdN2) reaction. It was shown that during 20-min
incubation at acid pH from 70 to 150 μg of the nanoparticles can be immobilized on 1 mg of the
microspheres depending on the components weight ratio Обсуждаются вопросы конструирования и применения композиционных материалов
на основе наноалмазов и биодеградируемых полигидроксиалканоатов. На примере
использования микросфер из 3-полигидроксибутирата (3-ПГБ) и модифицированных
наноалмазов (МНА) взрывного синтеза продемонстрирована возможность получения
комбинированного материала реакцией нуклеофильного присоединения по бимолекулярному
механизму AdN2. Показано, что при 20-минутной инкубации в кислых условиях на 1 мг
микросфер из биополимера может быть иммобилизовано от 70 до 150 мкг наночастиц в
зависимости от весового соотношения этих компонентов в реакции