The Research of Temperature Dependences of Electrical Conductivity and Thermopower of WS2 and WSe2 with Partial Replacement of W on Nb

Abstract

The temperature dependences of electrical conductivity and thermopower of tungsten disulfide and tung- sten diselenide have been investigated in this paper. These materials have the low value of electrical conductivity. The main idea of this paper is the increase of electrical conductivity for obtaining high thermoelectric efficiency. Niobium have served as an acceptor impurity. It has been revealed that the replacements of metal atoms have increased of electrical conductivity of W0:85Nb0:15Se2 by 4 order of magnitude. While the thermopower has decreased with increasing of impurity concentration. The ther- moelectric power factor has been calculated for materials. The figure of merit ZT of the best composition W0:95Nb0:05Se2 has been estimated and has had a value of 0.02 at room temperature.

В данной работе исследованы температурные зависимости электропроводности и термоЭДС дисульфида вольфрама и диселенида вольфрама. Так как данные материалы имеют низкую электропроводность, то основной целью данной работы было увеличение этого параметра, необходимого для высокой термоэлектрической эффективности. В качестве акцепторной примеси выступал ниобий. Было выявлено, что такое замещение увеличивает электропроводность материала на четыре порядка в образцах состава W0:85Nb0:15Se2. При этом термоЭДС уменьшается в зависимости от концентрации примеси. Измеренные параметры использовались для оценки термоэлектрического фактора мощности. Для наилучшего состава W0:95Nb0:05Se2 был оценен фактор добротности, который составил 0.02 при комнатной температуре