Influence of Chromium-Containing Al2О3 Nanopowders on Structural Modifications in Aluminum Oxide Micropowders

Abstract

Influence of an additive of chromium-containing Al2O3 nanopowders on phase transitions in aluminum oxide micropowder (a waste from alumina production) is investigated. Aluminum oxide nanopowders were synthesized by shock-wave method. Chromium compounds were introduced during the synthesis as well as following annealing of powders. Main difference between obtained chromium-containing Al2O3 nanopowders was their phase composition. Mixtures of nanopowders and alumina macropowders were pressed and sintered. The additive of the Al2O3 nanopowder that was dopped with chromium ions during the synthesis and is characterized by the prevalence of θ-phase is demonstrated to be the most perspective for ceramics fabrication on the alumina base

Исследовано влияние на фазовые превращения микропорошка оксида алюминия (отхода глиноземного производства) добавок хромсодержащих нанопорошков Al2О3. Нанопорошки оксида алюминия получали ударно-волновым синтезом, соединения хрома вводили как на стадии синтеза, так и при последующей термообработке порошков. Основное отличие полученных хромсодержащих нанопорошков Al2О3 заключалось в вариациях фазового состава. Смеси нанопорошков и микропорошка глинозема подвергали прессованию и спеканию. Показано, что для получения керамики на основе глинозема наиболее перспективно использование добавки нанопорошка оксида алюминия, легированного ионами хрома в условиях синтеза и характеризующегося преобладанием θ-фазы