Optical Absorption Evolution of Silver Nanocomposites with Arabinogalactan-g-Oligopyrrole Copolymer Matrix

Abstract

The optical absorption spectra measured of radically new nanocomposite of silver nanoparticles and arabinogalactan-g-oligopyrrole block-copolymer have 3 optical bands at 294, 426 and 585 nm. There have been no absorption maxima shifts but only absorption intensity decrease of the first and the sec- ond optical bands during eight months. Reduction of optical absorption intensity at 294 nm is related to decrease of acyl radical quantity in the nanocomposite. Decrease of 0D and 1D nanosilver plasmon absorption intensity at 426 nm can be explained by increase of the nanoparticle size in consequent to nanoparticle coalescence. Optical absorption of nanocomposite at 585 nm is associated with longitudal component of 1D nanosilver plasmon resonance and presence of plasmons in the oligopyrrole chains.

В спектрах оптического поглощения принципиально нового нанокомпозита серебра с привитым блок-сополимером арабиногалактан-олигопиррол, для которого характерны полосы поглощения при 294, 426, 585 нм, в течение восьми месяцев наблюдали снижение интенсивности погло- щения первых двух максимумов поглощения. Убывание интенсивности при 294 нм объясняет- ся уменьшением количества ацильных радикалов, возникающих в арабиногалактане при синтезе нанокомпозита. Снижение интенсивности плазмонного поглощения при 426 нм 0D- и 1D-наносеребра, возможно, связано с укрупнением частиц за счет их коалесценции. Оптическое поглощение нанокомпозита при 585 нм обусловлено продольной компонентой плазмонного резонанса 1D-наносеребра и наличием поляронов в олигопиррольных ветвях