Sulfation of Diethylaminoethyl Cellulose with Chlorosulfonic Acid in 1,4-dioxane
View/ Open:
URI (for links/citations):
https://elib.sfu-kras.ru/handle/2311/145624Author:
Kazachenko, Aleksandr S.
Vasilyeva, Natal’ya Yu.
Malyar, Yuriy N.
Elsufiev, Evgeniy V.
Berezhnaya, Yaroslava D.
Noureddine Issaoui
Казаченко, А. С.
Васильева, Н. Ю.
Маляр, Ю. Н.
Елсуфьев, Е. В.
Бережная, Я. Д.
Иссаоуи, Н.
Date:
2022-06Journal Name:
Журнал Сибирского федерального университета. Химия. Journal of Siberian Federal University. Chemistry 2022 15 (2)Abstract:
Sulfation of diethylaminoethylcellulose with chlorosulfonic acid in 1,4-dioxane was studied. It is shown that with an increase in the amount of chlorosulfonic acid and the duration of the process, an increase in the sulfur content in diethylaminoethylcellulose sulfate is observed. The maximum sulfur content (13.8 wt.%) in DEAE‑cellulose sulfate is observed at a ratio of ClSO3H:(DEAEC) of 20.22:1 (mmol: g) and a process duration of 180 min. The introduction of a sulfate group into the DEAEC molecule was confirmed by elemental analysis and FTIR spectroscopy. In the FTIR spectra of ethylaminoethylcellulose sulfate there are absorption bands related to stretching vibrations υ(C–O–S) at 810–815 cm‑1 and asymmetric stretching vibrations υas(O=S=O) at. 1249–1254 cm‑1. Using X‑ray phase analysis and optical microscopy, it was shown that during the sulfation of diethylaminoethylcellulose, amorphization of the material is observed. It has been shown by gel permeation chromatography that with an increase in the duration of the sulfation process, glycosidic bond cleavage reactions are also observed with the formation of products with a lower molecular weight and greater polydispersity Изучено сульфатирование диэтиламиноэтилцеллюлозы хлорсульфоновой
кислотой в 1,4-диоксане. Показано, что с увеличением количества хлорсульфоновой кислоты
и продолжительности п роцесса наблюдается увеличение содержания серы в сульфате
диэтиламиноэтилцеллюлозы. Максимальное содержание серы (13.8 мас.%) в сульфате
ДЭАЭ‑целлюлозы наблюдается при соотношении ClSO3H:(ДЭАЭЦ) 20,22:1 (ммоль: г) и
продолжительности процесса 180 мин. Введение сульфатной группы в молекулу ДЭАЭЦ-
подтверждено данными элементного анализа и ИК-Фурье-спектроскопии.
В ИК‑спектрах
сульфата этиламиноэтилцеллюлозы присутствуют полосы поглощения, относящиеся к валентным
колебаниям υ(C–O–S) при 810–815 см‑1 и асимметричным валентным колебаниям υas(O=S=O) при
1249–1254 см‑1. Методами рентгенофазового анализа и оптической микроскопией показано, что
в процессе сульфатирования диэтиламиноэтилцеллюлозы наблюдается аморфизация материала.
Методом гель-проникающей
хроматографии показано, что с увеличением продолжительности
процесса сульфатирования также наблюдаются реакции разрыва гликозидных связей
с образованием продуктов с меньшей молекулярной массой и большей полидисперсностью
Collections:
Metadata:
Show full item recordRelated items
Showing items related by title, author, creator and subject.
-
Preparation and Properties of Cellulosic Nanomaterials
Dufresne, Alain; Дюфрен, А. (Сибирский федеральный университет. Siberian Federal University, 2021-12)What are the reasons for the effervescence and explosion of the scientific literature during the last decade in the field of cellulosic and other polysaccharide nanomaterials? First, the raw materials are abundant, available ... -
Sulfation of Microcrystalline Cellulose with Sulfamic Acid in N,N-Dimethylformamide and Diglyme
Levdansky, Vladimir A.; Kondracenko, Alexandr S.; Levdansky, Alexandr V.; Kuznetsov, Boris N.; Djakovitch, Laurent; Pinel, Catherine; Левданский, В.А.; Кондрасенко, А.С.; Левданский, А.В.; Кузнецов, Б.Н.; Дьякович, Л.; Пинель, К. (Сибирский федеральный университет. Siberian Federal University., 2014-06)Sulfation of MCC by sulfamic acid in DMF or diglyme in the presence of urea was studied for the first time. It was established, that the degree of substitution in sulfated MCC was in the range from 1.40 to 1.54. It was ... -
Синтез и свойства органических гелей на основе таннинов коры лиственницы и целлюлозы древесины сосны
Микова, Н. М.; Иванов, И. П.; Жижаев, А. М.; Фетисова, О. Ю.; Кузнецов, Б. Н.; Mikova, Nadezhda M.; Ivanov, Ivan P.; Zhizhaev, Anatoliy M.; Fetisova, Ol’ga Yu.; Kuznetsov, Boris N. (Сибирский федеральный университет. Siberian Federal University, 2022-12)Разработан новый метод синтеза смешанных органических гелей на основе таннинов коры лиственницы и целлюлозы древесины сосны с использованием формальдегида в качестве сшивающего агента. Методами термогравиметрии, СЭМ, БЭТ ... -
Строение углеродных гелей, полученных карбонизацией органических ксерогелей на основе таннинов коры лиственницы и целлюлозы сосны
Микова, Н. М.; Иванов, И. П.; Жижаев, А. М.; Кузнецова, С. А.; Кузнецов, Б. Н.; Mikova, Nadezhda M.; Ivanov, Ivan P.; Zhizhaev, Anatoliy M.; Kuznetsova, Svetlana A.; Kuznetsov, Boris N. (Сибирский федеральный университет. Siberian Federal University, 2023-03)Впервые предложено получать углеродные гели путем карбонизации органических гелей, синтезированных золь-гель конденсацией формальдегида с таннинами коры лиственницы и целлюлозой сосны. По данным метода БЭТ, введение ... -
Synthesis and Functionalization of Bacterial Cellulose Nanocrystals from Kombucha Tea for Wound Dressing Applications
Elangwe, Collins N.; Morozkina, Svetlana N.; Uspenskaya, Mayya V.; Nguyen, Thanh H.; Dada, Kolawole S.; Элангвэ, К. Н.; Морозкина, С. Н.; Успенская, М. В.; Нгуен, Т. Х.; Дада, К. С. (Сибирский федеральный университет. Siberian Federal University, 2023-09)In this study, bacterial cellulose nanocrystals and aldehyde functionalized bacterial cellulose nanocrystals were synthesized from kombucha tea. Bacterial cellulose derived from kombucha tea is a biopolymer synthesized by ...