Magnetic and Structure Properties of CoPt-In₂O₃ Nanocomposite Films

Abstract

The structural and magnetic properties of CoPt-In₂O₃ nanocomposite films formed by vacuum annealing of the In/(Co3O4 + Pt)/MgO film system in the temperature range of 100–800 ◦C have been investigated. The synthesized nanocomposite films contain ferromagnetic CoPt grains with an average size of 5nm enclosed in an In2O3 matrix, and have a magnetization of 600 emu/cm3, and a coercivity of 150 Oe at room temperature. The initiation 200 ◦C and finishing 800 ◦C temperatures of synthesis were determined, as well as the change in the phase composition of the In/(Co3O4 + Pt)/MgO film during vacuum annealing

Исследованы структурные и магнитные свойства нанокомпозитных пленок CoPt- In₂O₃, полученных вакуумным отжигом пленочной системы In/(Co3O4 + Pt)/MgO в интервале температур 100 – 800 ◦C. Синтезированные нанокомпозитные пленки содержали ферромагнитные CoPt-кластеры со средним размером 5 nm, заключенные в матрицу In2O3, и имели намагниченность 600 emu/cm3, коэрцитивную силу 150 Oe при комнатной температуре. Определены температуры начала 200 ◦C и окончания 800 ◦C синтеза, а также изменение фазового состава пленки In/(Co3O4 + Pt)/MgO при вакуумном отжиге