Influence of TiO2 State on Oxidative Delignification of Aspen Wood and Wheat Straw

Abstract

The influence of preparation methods on structural characteristics of TiO2 catalysts was studied by the XRD, SEM, BET, DTA-DSC, FTIR techniques. Catalytic activity of obtained titanium dioxide samples was compared in reaction of oxidative delignification of aspen wood and wheat straw by hydrogen peroxide in acetic acid- water medium. The use of titanium dioxide in rutile modification allows to produce a cellulose product with lower content of a residual lignin, as compared to TiO2 in anatase modification. The increase of surface area of the TiO2 catalyst reduces its activity in wood and wheat straw delignification

Методами РФА, СЭМ, БЭТ, ДТА-ДСК, ИКС изучено влияние способов получения катализаторов TiO2 на их структурные характеристики. Сопоставлена каталитическая активность полученных образцов диоксида титана в реакции окислительной делигнификации древесины осины и соломы пшеницы пероксидом водорода в среде «уксусная кислота–вода». Использование диоксида титана в модификации рутил позволяет получить целлюлозный продукт с более низким содержанием остаточного лигнина, чем при использовании TiO2 в модификации анатаз. Увеличение удельной поверхности катализатора приводит к уменьшению степени делигнификации древесины осины и соломы пшеницы