The Stability of Sulfide Sorbents Based on Silica in Aqueous Media. Part ii. MCM-41 Matrix

Abstract

Sulfide sorbents based on MCM-41 have been synthesized. The chemical and thermal stability of the sorbents obtained has been investigated by physicochemical methods. It has been found that the acid treatment of the samples at the boiling point results in insignificant changes in structural, textural and sorption characteristics, demonstrating the total losses of the sorbent up to 15 wt%, which is considered to be connected with the dissolution of the malformed and unstructured particles of a silica matrix. The neutral and alkaline treatment induces more significant changes associated with the starting matrix dissolution (the weight loss is about 25-30 wt%). Nevertheless, the grafted organic functional layer is retained. The sorbents obtained are quite stable in the studied aggressive conditions and able to work over a long period of time in a variety of technological solutions and are not inferior to the well-known commercial sorbents with functional groups

Синтезированы сульфидные сорбенты на основе МСМ-41, исследована их химическая и термическая стабильность различными физико-химическими методами. Обнаружено, что кислотная обработка образцов при температуре кипения приводит к незначительным изменениям структурных, текстурных и сорбционных характеристик, демонстрируя общие потери сорбента до 15 масс.%. Указанный факт связан с растворением плохо сформированных и неструктурированных частиц кремниевой матрицы. Нейтральная и щелочная обработка приводит к более значительным изменениям, связанным с растворением исходной матрицы (потеря массы составляет около 25-30 масс.%). Тем не менее привитый органический функциональный слой сохраняется. Полученные сорбенты на основе МСМ-41, как и на основе SBA-15, относительно стабильны в изученных агрессивных условиях и способны работать в течение длительного периода времени в различных технологических растворах