Texture Properties, Phase Composition and Morphology of Supported Ni-Mo /γ-Al2O3 Systems

Abstract

The synthesis of supported systems containing Ni and Mo has been carried out. The support was an industrial powder of aluminum oxide (γ-Al2O3) obtained from pseudoboehmite by heat treatment. One of the key features is the use of an alcoholic solution of molybdenum blue obtained using the mechanical activation method as a source of molybdenum. The synthesized systems are supposed to be used in hydroprocesses for the processing of crude oil in order to remove heteroatomic compounds (in particular, sulfur- and nitrogen- containing ones). The physicochemical properties of the obtained samples were also observed, It was shown that the morphology of the support is completely inherited from the predecessor

Проведен синтез нанесенных систем, содержащих Ni и Mo. В качестве носителя выступал промышленный порошок оксида алюминия (γ- Al2O3), полученный из псевдобемита методом термической обработки. Одной из ключевых особенностей является использование в качестве источника молибдена спиртового раствора молибденовой сини, полученной с привлечением метода механоактивации. Синтезированные системы предполагается использовать в гидропроцессах переработки нефтяного сырья с целью удаления гетероатомных соединений (в частности серо- и азотсодержащих). Также были исследованы физико- химические свойства полученных образцов, было показано, что морфология носителя полностью наследуется от предшественника