Plasma-chemical synthesis of Fe3O4 nanoparticles for doping of high-temperature superconductors

Abstract

Ferrite nanoparticles (Fe3O4) have been produced by the direct low-pressure plasma-chemical synthesis. X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), vibration magnetometry (VSM), and Mössbauer spectroscopy (NGR) were used for measurements, showing that the produced nanoparticles have an average size of 9.4 nm, a crystalline phase of magnetite, possess a property of superparamagnetism at room temperature, and have a blocking temperature of 89 K. The peculiarities of nanoparticle behavior in the magnetic field, related to a large specific surface area, are discussed.