Spectroscopic properties of HoFe3(BO3)4, NdFe3(BO3)4 and Ho0.75Nd0.25Fe3(BO3)4 single crystals
Автор | Sukhachev, A. L. | |
Автор | Malakhovskii, A. V. | |
Автор | Aleksandrovsky, A. S. | |
Автор | Gudim, I. A. | |
Автор | Temerov, V. L. | |
Дата внесения | 2019-07-01T07:30:28Z | |
Дата, когда ресурс стал доступен | 2019-07-01T07:30:28Z | |
Дата публикации | 2018 | |
Библиографическое описание | Sukhachev, A. L. Spectroscopic properties of HoFe3(BO3)4, NdFe3(BO3)4 and Ho0.75Nd0.25Fe3(BO3)4 single crystals [Текст] / A. L. Sukhachev, A. V. Malakhovskii, A. S. Aleksandrovsky, I. A. Gudim, V. L. Temerov // Optical Materials. — 2018. — Т. 83. — С. 87-92 | |
ISSN | 09253467 | |
URI (для ссылок/цитирований) | https://www.sciencedirect.com/science/article/pii/S0925346718303550?via%3Dihub | |
URI (для ссылок/цитирований) | https://elib.sfu-kras.ru/handle/2311/111565 | |
Аннотация | Polarized absorption spectra of ferroborates HoFe3(BO3)4, NdFe3(BO3)4 and Ho0.75Nd0.25Fe3(BO3)4 were measured at room temperature in spectral range 4000–24500 cm−1 (400–2500 nm). The studied single crystals were grown from solution-melts. Intensities of the f-f transitions were measured and the Judd–Ofelt parameters Ωλ of Ho3+ and Nd3+ ions in the studied crystals were calculated. It was revealed that the crystals content not strongly influences the Judd–Ofelt parameters. The Ω2 parameter for Ho3+ ion is the most sensitive to the crystal content. Linear dichroism of the hypersensitive transitions appeared to be the largest one for both rare earth ions. | |
Тема | Holmium and neodymium ferroborates | |
Тема | Judd–Ofelt parameters | |
Название | Spectroscopic properties of HoFe3(BO3)4, NdFe3(BO3)4 and Ho0.75Nd0.25Fe3(BO3)4 single crystals | |
Тип | Journal Article | |
Тип | Journal Article Preprint | |
Страницы | 87-92 | |
ГРНТИ | 29.31.21 | |
Дата обновления | 2019-07-01T07:30:28Z | |
DOI | 10.1016/j.optmat.2018.05.078 | |
Подразделение | Институт нанотехнологий, спектроскопии и квантовой химии | |
Журнал | Optical Materials | |
Квартиль журнала в Scopus | Q1 | |
Квартиль журнала в Web of Science | Q2 |