Radical Copolymerization of Styrene and α-angelicalactone: Synthesis and Properties of the Obtained Copolymers
Author:
Kaigorodov, Konstantin L.
Tarabanko, Valery E.
Pashenova, Nataliya V.
Loskutov, Sergei R.
Voronchikhin, Vasiliy D.
Smirnova, Marina A.
Chesnokov, Nikolay V.
Кайгородов, К. Л.
Тарабанько, В. Е.
Пашенова, Н. В.
Лоскутов, С. Р.
Ворончихин, В. Д.
Смирнова, М. А.
Чесноков, Н. В.
Date:
2023-06Journal Name:
Журнал Сибирского федерального университета.Химия. Journal of Siberian Federal University. Chemistry 2023 16(2)Abstract:
Biodegradation ability of synthetic polymer materials is an urgent problem of modern ecology
situation. A known new biodegradable polymer is polyangelicalactone (PAL). In this paper, styrene-α-
angelicalactone copolymers were obtained by radical polymerization. The resulting copolymers have
physical and mechanical properties similar to those of polystyrene and its graft-copolymers
with PAL.
Both they were mechanically destroyed when incubated in gray forest soil over 28 weeks. The obtained
results show that the modification of polystyrene with the impurities of α-angelicalactone
does not
worsen the mechanical properties of the copolymers but instead gives them biodegradation abilities В настоящей работе получены сополимеры стирола и α-ангеликалактона
методом
радикальной полимеризации. Полученные сополимеры имеют физико-механические
свойства,
аналогичные свойствам
полистирола и его привитых сополимеров с полиангеликалактоном. Оба
полимера механически разрушаются при инкубации в серой лесной почве в течение 28 недель.
Полученные результаты показывают, что модификация полистирола примесями α-ангеликалактона
не ухудшает механические свойства
сополимеров и придает им способность к биоразложению