Nanodispersed Powders of Fe-Ni Particles with Carbon Shell
View/ Open:
URI (for links/citations):
https://elib.sfu-kras.ru/handle/2311/34767Author:
Churilov, Grigory N.
Vnukova, Natalia G.
Nikolaev, Nikita S.
Glushenko, Gari A.
Osipova, Irina V.
Lopatin, Vladislav A.
Komogortsev, Sergey V.
Velikanov, Dmitry A.
Volochaev, Mikhail N.
Nemtsev, Ivan V.
Чурилов, Григорий Н.
Внукова, Наталья Г.
Николаев, Никита С.
Глущенко, Гари А.
Осипова, Ирина В.
Лопатин, Владислав А.
Комогорцев, Сергей В.
Великанов, Дмитрий А.
Волочаев, Михаил Н.
Немцев, Иван В.
Date:
2017-12Journal Name:
Журнал Сибирского федерального университета. Математика и физика. Journal of Siberian Federal University. Mathematics & Physics;2017 10 (4)Abstract:
The initial carbon condensate containing nickel-iron nanoparticles with a graphite conversion was syn-
thesized in the high-frequency carbon-helium arc plasma at ambient pressure. The nickel-iron particles
were extracted by the treatment of the carbon condensate with nitric and hydrochloric acids. Undissolved
residue and dissolved sample were received. Undissolved residue has both the structure and magnetic
properties of (MR/Ms = 0.30, Hc = 270 Oe). Lack of hysteresis loops for the dissolved sample shown
that metals are in the paramagnetic state Исходный углеродный конденсат, содержащий железоникелевые наночастицы с углеродной обо-
лочкой, был синтезирован в углеродно-гелиевом дуговом ВЧ–разряде при атмосферном давлении.
Железоникелевые частицы были выделены обработкой углеродного конденсата азотной и гидро-
хлоридной кислотами. В результате были получен нерастворимый остаток и растворимый об-
разец. Нерастворимый остаток имеет как структурные, так магнитные характеристики (MR
/ Ms = 0.30, Hc = 270 Oe). Растворимый образец продемонстрировал отсутствие петли гисте-
резиса, что характерно для металлов в парамагнитном состоянии