Связующие свойства лигнинов, полученных при окислительной каталитической делигнификации древесины и соломы

Abstract

Composition and binding properties of acetic acid lignins obtained at oxidative catalytic delignification of different types of plant biomass (softwood, hardwood, wheat straw) in the medium: acetic acid - hydrogen peroxide - water - sulfuric acid catalyst were compared. Obtained acetic acid lignins have high concentration of reactive oxygen-containing functional groups, therefore they can be used as low-toxic binding agent for production of wood panel materials with good strength characteristics. The influence of lignin nature, its content in lignin/wood blend and conditions of pressing on the bending strength and water-resistance of obtained wood panel materials was studied. Optimal technological parameters for manufacture of strong and water steady wood panels were found.

Сопоставлены состав и связующие свойства лигнинов, полученных в качестве побочных продуктов при окислительной каталитической делигнификации различных видов растительной биомассы (хвойная и лиственная древесина, солома пшеницы) в среде уксусная кислота - перокисид водорода - вода - серно-кислотный катализатор. Получаемые уксусно-кислотные лигнины имеют высокую концентрацию реакционных кислород-содержащих групп, что позволят их использовать в качестве низкотоксичных связующих веществ для производства древесных плитных материалов с хорошими прочностными характеристиками. Изучено влияние природы лигнина, его содержания в смеси лигнин/древесина и условий прессования на прочность и водостойкость получаемых древесных панелей. Установлены оптимальные технологические параметры для производства прочных и устойчивых к действию влаги древесных плитных материалов.