Biomedical Studies of Polyhydroxyalkanoates

Abstract

The paper describes research of biomedical applications of experimental polymer devices prepared from polyhydroxyalkanoates (PHAs) in the Institute of Biophysics SB RAS and Siberian Federal University (Krasnoyarsk, Russia) between 2000 and 2012. The high-purity PHA specimens were investigated and then used to prepare surgical sutures, 2D and 3D dense and porous matrices, fully resorbable tubular stents, and polymer coatings. The polymer devices that differed in their shape and mass were introduced into muscles, bones, blood vessels, and internal organs in order to investigate the response of tissues with different structure to the implants. The studies showed that PHAs were highly biocompatible with different tissues and their implantation for extended periods of time did not induce adverse responses of the blood system, cells, tissues, or the entire organism. The authors proved that PHAs can be effectively used as prosthetic implants and bone-replacing implants

В статье представлены результаты исследований экспериментальных полимерных изделий, полученных из полигидроксиалканоатов (ПГА), выполненных в Институте биофизики СО РАН и Сибирском федеральном университете в период 2000-2012 гг. Из высокоочищенных ПГА разработаны и исследованы хирургические нити, резорбируемые трубчатые стенты, 2D и 3D плотные и пористые матриксы, полимерные покрытия. Полимерные изделия различной формы и массы были имплантированы в мышцы, костную ткань, внутривенно, во внутренние органы и исследован ответ тканей на различные имплантаты. Исследования показали, что ПГА обладают высокой биосовместимостью по отношению к различным тканям и их имплантация на длительные сроки не вызывает реактивных изменений со стороны клеток, тканей и крови. Авторы показали, что ПГА перспективны в качестве различных тканевых имплантатов и костнопластических материалов