Crystal Structure and Magnetic Properties in Pyroxenes Li0.7Na0.3FeGe2O6
View/ Open:
URI (for links/citations):
https://elib.sfu-kras.ru/handle/2311/19700Author:
Drokina, Tamara V.
Petrakovskii, German A.
Velikanov, Dmitrii A.
Molokeev, Maxim S.
Rezina, Elena G.
Дрокина, Тамара В.
Петраковский, Герман А.
Великанов, Дмитрий А.
Молокеев, Максим С.
Резина, Елена Г.
Date:
2015-08Abstract:
The Li0,7Na0,3FeGe2O6 solid solution has been synthesized by the solid-phase reaction. The clinopy-
roxene compound has been investigated by X-ray diffraction and by bulk magnetic measurements. The
structural properties of the cation substitution compound are presented. Using SQUID techniques the tem-
perature dependence of the magnetic susceptibility was measured. It exhibits a sharp maximum, which is
suggested the phase transition from the paramagnetic state to a magnetically ordered state below 15.5 K
in the sample of pyroxene solid solution Поликристаллические образцы Li0,7Na0,3FeGe2O6 были получены твердофазным синтезом и ис-
следованы методами рентгеновской дифракции и СКВИД-метрии. Представлены характеристи-
ки структурных свойств. Показано, что температурная зависимость магнитной восприимчиво-
сти при температуре 15,5 К имеет излом, характерный для переходов в магнитоупорядоченное
состояние