Influence of Nanomodifying Additives and Strengthening Phase on the Structure and Properties of Laser Coating of Porous Titanium

Abstract

The results of an experimental study of the influence of nanomodifying additives on the structure and mechanical properties of coatings during laser surfacing of a composite powder with a strengthening phase on porous titanium are presented. Titanium alloy of the Ti–V–Al system with a strengthening phase of titanium carbide was used as a surfacing material, and nano-sized refractory titanium nitride powders were used as a modifying additive. An analysis of the morphological and structural characteristics of a deposited single track was carried out, and the influence of modifying additives on the intensity of dissolution of the strengthening phase and the mechanical characteristics of the deposited layer was established

Приведены результаты экспериментального исследования влияния наномодифицирующих добавок на структуру и механические свойства покрытий при лазерной наплавке ком- позиционного порошка с упрочняющей фазой. В качестве наплавочного материала использовался титановый порошок системы Ti–V–Al с упрочняющей фазой из карбида титана, а в качестве модифицирующей добавки — наноразмерный тугоплавкий порошок нитрида титана. Проведен анализ морфологических и структурных характеристик наплавленного одиночного трека, установлено влияние модифицирующих добавок на интенсивность растворения упрочняющей фазы и механические характеристики наплавленного слоя