Study of New Composite Materials Based on Epoxy Resin with Photoluminescence Effect

Abstract

Strontium aluminate doped with europium with various particle sizes was added to epoxy resins ED-20 and Crystal 85-5 in a mass concentration of 0% to 17%. Mechanical tests for three-point bending and instrumental indentation were carried out. The dependences of the modulus of elasticity and hardness on the concentration of the filler are obtained. The photoluminescent properties of the resulting composites have been studied. The dependences of the luminescence intensity and decay time on the content of composite components are established

Алюминат стронция, легированный европием с различным размером частиц, был добавлен в эпоксидные смолы ЭД-20 и Crystal 85-5 в массовой концентрации от 0% до 17%. Проведены механические испытания на трехточечный изгиб и инструментальное индентирование. Получены зависимости модуля упругости и твердости от концентрации наполнителя. Исследованы фотолюминесцентные свойства полученных композитов. Установлены зависимости интенсивности люминесценции и времени затухания от содержания компонентов в композите