The Influence of Thallium Additives on the Kinetics of Oxidation of the Zn22Al Alloy

Abstract

The article presents the results of a thermogravimetrical study of the effect of thallium alloying additives on the oxidation kinetics of the Zn22Al alloy. Established in the temperature range of 473–623 K the kinetic and energy parameters of the oxidation of alloys. The oxidation of alloys proceeds according to the hyperbolic mechanism and has the order of 10–4 kg∙m‑2∙sec‑1. Higher activation energies indicate that the oxidation of these alloy samples results in the formation of oxide films with good protective properties. Additives of thallium in amounts of 0.01–1.0 wt.% contribute to a decrease in the oxidizability of the Zn22Al alloy. The resulting products during the oxidation of the studied alloys consist of a mixture of oxides ZnO, ZnAl2O4, Al2O3, Tl2O3

В статье приведены результаты термогравиметрического исследования влияния легирующих добавок таллия на кинетику окисления сплава Zn22Al. В интервале температур 473–623 K установлены кинетические и энергетические параметры процесса окисления сплавов. Окисление сплавов протекает по гиперболическому механизму и имеет порядок 10–4 кг∙м‑2∙сек‑1. Более высокие значения энергий активации свидетельствуют о том, что при окислении данных образцов сплавов образуются оксидные пленки с хорошими защитными свойствами. Добавки таллия в количествах 0.01–1.0 мас.% способствуют уменьшению окисляемости сплава Zn22Al. Образующиеся продукты при окислении изученных сплавов состоят из смеси оксидов ZnO, ZnAl2O4, Al2O3, Tl2O3