Anodic Behavior of Zn22Al Alloy, Doped with Erbium

Abstract

The article presents the results of a potentiodynamic study of the anodic behavior of the Zn22Al alloy with erbium dopants in various corrosive media of HCl, NaCl and NaOH electrolytes. Erbium alloying additions corrosion rate in various corrosive environments. In this case, there is a shift in the potentials in amounts of 0.01÷1.0 wt.% somewhat increase the anode resistance of the Zn22Al alloy by reducing the of corrosion, pitting formation and repassivation of alloys to the region of positive values. The dynamics of changes in electrochemical potentials favorably affects the parameters of the corrosion resistance of alloys. Erbium additions monotonically reduce the corrosion rate of the anode Zn22Al alloy in various media

В статье приведены результаты потенциодинамического исследования анодного поведения сплава Zn22Al с легирующими добавками эрбия в различных коррозионных средах электролитов HCl, NaCl и NaOH. Легирующие добавки эрбия в количествах 0.01÷1.0 мас.% несколько повышают анодную устойчивость сплава Zn22Al за счет уменьшения скорости коррозии в различных коррозионных средах. При этом наблюдается смещение потенциалов коррозии, питтингообразования и репассивации сплавов в область положительных значений. Динамика изменения электрохимических потенциалов благоприятно влияет на параметры коррозионной стойкости сплавов. Добавки эрбия монотонно снижают скорость коррозии анодного сплава Zn22Al в различных средах