The Physicochemical Analysis of Bayerite Al(OH)3 → γ-Al2O3 Transformation

Abstract

It was obtained aluminum hydroxide in the form of bayerite by precipitation with ammonia. The precipitation pH was found by the potentiometric titration. Based on the data of thermal, X‑ray diffraction and IR‑analysis it was identified the sequence of bayerite transitions up to 800 °C. The study of nitrogen adsorption- desorption allowed to determine a specific surface, a volume, and dimensions of pores for boehmite and γ- Al2O3 as 135±2 and 238±10 m2/g; 0.38 and 0.51 cm3/g; 1.7 and 3.8 nm, relatively. The value of effective activation energy for boehmite →γ- Al2O3 transition ((136±5) kJ/mol) was found by means of non- isothermal method (by Avrami equation)

Получен гидроксид алюминия в виде байерита осаждением аммиаком. рН осаждения определен методом потенциометрического титрования. На основании данных термического, рентгенофазового и ИК‑спектрального анализа установлена последовательность превращений байерита в интервале температур до 800 °C. По данным адсорбции-десорбции азота для образующихся бёмита и γ-Al2O3 определена удельная поверхность, объем и средний размер пор: 135±2 и 238±10 м2/г; 0,38 и 0,51 см3/г; 1,7 и 3,8 нм соответственно. Неизотермическим методом (по уравнению Аврами) оценена эффективная энергия активации перехода байерит→бёмит: (136±5) кДж/моль