The Study of the Fine Structure of Ti-Al Coatings on the Surface of Ti, Obtained by Mechanical Alloying

Abstract

The work is devoted to the study of structural-phase transformations in composite coatings (Ti-Al)+Ti during mechanical alloying. The data on the structural-phase states of (Ti-Al)-Ti coatings after mechanical alloying have been obtained, confirming the mechanism of formation of the modified layer due to deformation compaction of powder particles on the titanium surface under mechanical action. As a result of mechanochemical fusion, a TiAl3 phase with a bcc lattice (I4=mmm structure) was detected, which corresponds to the stable state of the TiAl3 alloy. Under conditions of mechanical alloying of the structure, I4=mmm transforms into the L12 structure, which corresponds to the metastable state of TiAl3

Работа посвящена исследованию структурно-фазовых превращений в композиционных покрытиях (Ti-Al)+Ti при механическом сплавлении. Получены данные о структурно- фазовых состояниях (Ti-Al)-Ti покрытий после механического сплавления, подтверждающие механизм формирования модифицированного слоя за счет деформационного уплотнения частиц порошка на поверхности титана под механическим воздействием. В результате механохимического сплавления обнаружена фаза TiAl3 с ОЦК-решеткой (структура I4=mmm), что соответствует стабильному состоянию сплава TiAl3. В условиях механического сплавления структура I4=mmm переходит в структуру L12, что соответствует метастабильному состоянию TiAl3.