Magnetic and Structure Properties of CoPt-In₂O₃ Nanocomposite Films
URI (for links/citations):
https://elib.sfu-kras.ru/handle/2311/135357Author:
Bykova, Liudmila E.
Myagkov, Victor G.
Zhigalov, Victor S.
Matsynin, Alexei A.
Velikanov, Dmitry A.
Bondarenko, Galina N.
Patrin, Gennady S.
Быкова, Людмила Е.
Мягков, Виктор Г.
Жигалов, Виктор С.
Мацынин, Алексей А.
Великанов, Дмитрий А.
Бондаренко, Галина Н.
Патрин, Геннадий С.
Date:
2020-08Journal Name:
Журнал Сибирского федерального университета.Математика и физика.Journal of Siberian Federal University. Mathematics & Physics, 2020 13 (4)Abstract:
The structural and magnetic properties of CoPt-In₂O₃ nanocomposite films formed by
vacuum annealing of the In/(Co3O4 + Pt)/MgO film system in the temperature range of 100–800 ◦C
have been investigated. The synthesized nanocomposite films contain ferromagnetic CoPt grains with
an average size of 5nm enclosed in an In2O3 matrix, and have a magnetization of 600 emu/cm3, and a
coercivity of 150 Oe at room temperature. The initiation 200 ◦C and finishing 800 ◦C temperatures of
synthesis were determined, as well as the change in the phase composition of the In/(Co3O4 + Pt)/MgO
film during vacuum annealing Исследованы структурные и магнитные свойства нанокомпозитных пленок CoPt-
In₂O₃, полученных вакуумным отжигом пленочной системы In/(Co3O4 + Pt)/MgO в интервале
температур 100 – 800 ◦C. Синтезированные нанокомпозитные пленки содержали ферромагнитные
CoPt-кластеры со средним размером 5 nm, заключенные в матрицу In2O3, и имели намагниченность 600 emu/cm3, коэрцитивную силу 150 Oe при комнатной температуре. Определены температуры начала 200 ◦C и окончания 800 ◦C синтеза, а также изменение фазового состава пленки
In/(Co3O4 + Pt)/MgO при вакуумном отжиге