• русский
    • English
  • English 
    • русский
    • English
    View Item 
    •   DSpace Home
    • Научные журналы
    • Журнал СФУ. Техника и технологии. Journal of SibFU. Engineering & Technologies
    • Техника и технологии. Engineering & Technologies. 2020 13 (4)
    • View Item
    •   DSpace Home
    • Научные журналы
    • Журнал СФУ. Техника и технологии. Journal of SibFU. Engineering & Technologies
    • Техника и технологии. Engineering & Technologies. 2020 13 (4)
    • View Item
    JavaScript is disabled for your browser. Some features of this site may not work without it.

    Повышение износостойкости изделий из аустенитных сталей путем совмещения технологий цементации и диффузионного легирования в среде легкоплавких жидкометаллических расплавов

    Thumbnail
    View/Open:
    11_Sokolov.pdf (366.1 Kb)
    DOI:
    10.17516/1999-494X-0241
    URI (for links/citations):
    http://elib.sfu-kras.ru/handle/2311/135345
    Author:
    Соколов, А.Г.
    Бобылёв, Э.Э.
    Sokolov, Aleksandr G.
    Bobylyov, Eduard E.
    Date:
    2020-06
    Journal Name:
    Журнал Сибирского федерального университета. Техника и технологии. Journal of Siberian Federal University. Engineering & Technologies, 2020, 13 (4)
    Abstract:
    Данная статья посвящена исследованию влияния совмещения технологий цементации и диффузионной металлизации никелем и хромом в среде Pb-Bi-Li сталей аустенитного класса. Технология состоит из предварительной цементации, диффузионного насыщения и окончательной цементации. Предложенная технология позволяет увеличить микротвердость поверхностных слоев изделий из сталей аустенитного класса до 19500 МПа. Свойства полученных покрытий зависели от температуры и длительности технологического воздействия на каждом этапе. При увеличении температуры наблюдалось снижение микротвердости покрытия. При увеличении длительности возрастала толщина покрытия
     
    This paper investigated the overlap of carburization and diffusion saturation from liquid metal medium solutions technologies. The carburization of austhenic steel able to increase of its wear resistance and microhardness to 700HV. But this kind of treatment provided to reduction of corrosion resistance. This effect conditioned by formation of chromium carbides, herewith austenite of steel impoverished of chromium. This paper proposes the new technology lets increase the durability of asthenic steels, using carburization and diffusion saturation in eutectic Pb-Bi-Li medium with adding of nickel and chromium. The most effective technology consisted of previous carburization, diffusion saturation and final carburization. First carburization provided to increase of surface layers microhardness to 2800 MPa, diffusion saturation to 7500 MPa, the final carburization to 19500 MPa. The properties of coating depended of combination of technological impact and technological modes of every stage of technological process: temperature and duration. The temperature influenced to microhardness of coating: when the temperature increased microhardness decreased. The duration of diffusion saturation influenced to thickness of diffusion layer: when the duration increased the thickness increased too
     
    Collections:
    • Техника и технологии. Engineering & Technologies. 2020 13 (4) [11]
    Metadata:
    Show full item record

    DSpace software copyright © 2002-2015  DuraSpace
    Contact Us | Send Feedback
    Theme by 
    @mire NV
     

     


    DSpace software copyright © 2002-2015  DuraSpace
    Contact Us | Send Feedback
    Theme by 
    @mire NV