Magnetic Properties of Fe₁₋ₓCoₓSi Single Crystals at Low Co Impurity Concentrations
Скачать файл:
URI (для ссылок/цитирований):
https://elib.sfu-kras.ru/handle/2311/109336Автор:
Yurkin, Gleb Yu.
Patrin, Gennady S.
Yarikov, Stanislav A.
Юркин, Глеб Ю.
Патрин, Геннадий С.
Яриков, Станислав А.
Дата:
2019-02Журнал:
Журнал Сибирского федерального университета. Математика и физика. Journal of Siberian Federal University. Mathematics & Physics; 2019 12 (1)Аннотация:
Magnetostatic properties of FeSi and Fe0;98Co0;02Si single crystals have been studied. It has been found
that the temperature and field dependences of the magnetization of monocrystal FeSi are strongly affected
by introduction of a small amount of Co (2 %). A description of the results were provided by a model ac-
counting for the formation of superparamagnetic iron clusters, as well as Fe-Co complexes. It is assumed
that Fe-Co complexes form a ferromagnetic phase, which is approximately 0.6% of the Fe0;98Co0;02Si
sample weight В работе представлено исследование магнитостатических характеристик образцов FeSi и
Fe0;98Co0;02Si. Обнаружено, что внесение небольшого количества примести Co (2 %) значительно влияет на температурные и полевые зависимости намагниченности монокристалла FeSi.
Результаты обработаны в рамках модели, учетывающей образование суперпарамагнитных кластеров железа, а также комплексов Fe-Co. Предполагается, что комплексы Fe-Co образуют
ферромагнитную фазу, которая составляет примерно 0,6 % от массы образца Fe0;98Co0;02Si.