Thermodynamic Stability of Intermetallic Compounds in Technical Aluminum
View/ Open:
URI (for links/citations):
https://elib.sfu-kras.ru/handle/2311/10345Author:
Begunov, Albert I.
Kuz’min, Mikhail P.
Бегунов, А.И.
Кузьмин, М.П.
Date:
2014-03Abstract:
For the following systems Al-Ti, Al-Ni, Al-Zr, Al-Cr, Al-Fe, Al-V the wide range of intermetallic
compounds based on aluminum was considered. Thermodynamic parameters such as Gibbs energy
and formation enthalpy characterizing the properties of resulting intermetallic compounds were
calculated. The relations of these two characteristics versus temperature were established in a wide
range. On the basis of the obtained relations the comparative assessment of the compound stability for
each binary system was carried out. The level of each intermetallic compound stability was revealed
on the ground of the affinity with aluminum. The possibilities of practical application of obtained data
for actual metallurgical tasks were defined Рассмотрен широкий ряд интерметаллических соединений систем Al-Ti, Al-Ni, Al-Zr, Al-Cr,
Al-Fe, Al-V. Рассчитаны такие термодинамические характеристики, как энергия Гиббса и
энтальпия образования, характеризующие свойства образующихся интерметаллических
соединений. Установлены зависимости данных характеристик от температуры в широком
диапазоне. На основании полученных зависимостей проведена сравнительная оценка
устойчивости интерметаллических соединений для каждой системы. Показана степень
устойчивости каждого интерметаллида исходя из его сродства к алюминию