Hydrodynamic Dispersion of Calcium Aluminosilicate from Technogenic and Nonmetallic Materials

Abstract

Physicochemical properties of two calcium aluminosilicate materials after reducing in the hydrodynamic rotary generator in supercavitation mode were studied. The samples are the crystal ceramic foam based on Kansko-Achinsk lignite-ash and the porous glass material obtained from low-manganese nonmetallic feed. X-ray phase analysis, EPR-method, NPR-method (the Mossbauer Effect) and optical microscopy were used. It was found that the material is changing its stucrure in a hydrodynamic dispersion process caused by high-cavitation. The nature of the changes depends on its initial state

Изучены физико-химические свойства двух кальций-алюмосиликатных материалов после измельчения в гидродинамическом генераторе роторного типа в режиме суперкавитации. Исследованы образцы – кристаллическая пенокерамика на основе зол бурых Канско-Ачинских углей и пористый стекломатериал, полученный из нерудного сырья с низким содержанием марганца. Для анализа были использованы методы РФА, ЭМР, ЯГР (эффект Мёссбауэра), оптическая микроскопия. Показано, что в процессе гидродинамического диспергирования за счет высокоэнергетического кавитационного воздействия в материалах происходят глубокие структурные изменения. Получено, что характер изменений зависит от исходного состояния исследуемого материала