Characteristic Physical–Mechanical and High–Temperature Electric Properties Semicinductor Ceramic Based SnO2 with Addition MnO2 and CuO

Abstract

Ceramic semiconductor SnO2-based materials with MnO2 and CuO additives were synthesized at 1300 ºС and 1400 ºС. There has been carried out an investigation of the physical–mechanical and high–temperature electric properties. As a result, sintering of the material with MnO2 additive is shown to be improved at increasing firing temperature. The composition 96 % SnO2-2 % Sb2O3-2 % CuO made at the temperature 1300 ºС has the best electrophysical properties (its resistivity is 0.09 mOhm m). The resistivity of the 94 % SnO2-2 % Sb2O3-2 % CuO-2 % MnO2 composition in the hightemperature region is more by a factor of 3. The 96 % SnO2-2 % Sb2O3-2 % MnO2 composition has nonlinear voltage-currant characteristic, and hysteresis is present

Синтезированы керамические полупроводниковые материалы на основе диоксида олова с добавками MnO2 и CuO. Температуры синтеза были 1300 и 1400 ºС. Проведены исследования физико-механических и электрофизических свойств. Показано, при повышении температуры обжига для материала, полученного при использовании MnO2, происходит существенное улучшение спекания. Наилучшими электрофизическими характеристиками обладают образцы состава 96%SnO2-2%Sb2O3-2%CuO полученные при температуре обжига 1300 ºС(УЭС 0,09 мОм×м). УЭС состава 94%SnO2-2%Sb2O3-2%CuO-2%MnO2 в высокотемпературной области выше в 3 раза. Для состава 96%SnO2-2%Sb2O3-2%MnO2 вольтамперная характеристика имеет нелинейный вид и присутствует гистерезис